An analysis of the impact of the FDM technology parameters on tribological properties
The paper presents the results of tribological tests for sample models made by FDM technology. The ringshaped samples were made of the ABS P430 material using the Dimension 1200es machine. Disc-shaped counter-samples were made of C45 steel. The analysed technological parameter of the process of building sample models was the “printing” direction (between the friction surface of the sample and the building platform), determined at three degrees of variability (0°, 45°, and 90°). Using the T-15 tribological tester of the ring-on- disc type, a study was carried out to determine the effect of printing direction on the friction force and the total friction wear. In addition, metrological measurements of the tested surfaces were carried out.
Przedstawiono wyniki badań tribologicznych modeli próbek wykonanych w technologii FDM osadzania topionego materiału. Próbki w kształcie pierścieni wykonane zostały z materiału ABS P430 przy wykorzystaniu maszyny Dimension 1200es. Przeciwpróbki wykonane zostały ze stali C45 w kształcie tarczy. Analizowanym parametrem technologicznym procesu budowy modeli próbek był kierunek „wydruku” (pomiędzy płaszczyzną tarcia próbki a platformą budowania), ustalony na trzech stopniach zmienności (0°, 45° i 90°). Wykorzystując tester tribologiczny T-15 typu pierścień–tarcza, przeprowadzono badania polegające na wyznaczeniu wpływu kierunku rozmieszczenia modeli na platformie budowania na wartość siły tarcia oraz sumaryczne zużycie pary ciernej. Ponadto przeprowadzone zostały pomiary metrologiczne badanych powierzchni.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).