Estimation Of Cooling Rates In Suction Casting And Copper-Mould Casting Processes
The cooling rates associated with suction and copper-mould casting of ø2, ø3 and ø5 mm rods made in Fe-25wt%Ni and Al-33wt%Cu alloys were determined based on their cellular and lamellar spacings, respectively. The work showed that the temperature profile in cylindrical samples can not be determined merely by microstructural examination of eutectic sample alloys. A concave solidification front, as a result of eutectic transformation, caused decrease of a lamellar spacing while approaching to the rod centre. The minimum axial cooling rates, estimated based on the cellular spacing in the Fe-25wt%Ni alloy, were evaluated to be about 200 K/s for both ø2 and ø3 mm and only 30 K/s for the ø5 mm suction cast rods. The corresponding values were slightly lower for the copper-mould cast rods.
Na podstawie analizy wielkości dendrytów komórkowych w stopie Fe-25Ni i odległości międzypłytkowych w stopie Al-33Cu zostały oszacowane szybkości chłodzenia w trakcie odlewania stopów metodami suction casting i copper-mould casting. Badania wykazały, że rozkład szybkości chłodzenia w cylindrycznych próbkach nie może być oszacowany w stopach z krystalizacją eutektyczną. W tym przypadku bowiem dochodzi do zmniejszania odległości międzypłytkowej w miarę zbliżania się do osi pręta, ze względu na wklęsły charakter frontu krystalizacji. Minimalna szybkość chłodzenia w osi prętów odlanych za pomocą metody suction casting, wyznaczona w oparciu o pomiary wielkości dendrytów komórkowych w stopie Fe-25wt%Ni, wyniosła ok. 200 K/s dla stopów o średnicy ø2 i ø3 mm, i tylko 30 K/s dla stopów o średnicy ø5 mm. W przypadku stopów odlanych metodą copper-mould casting oszacowane wartości były nieznacznie mniejsze.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.