Preliminary feasibility analysis of microwave sintering of lunar regolith simulant at glass softening temperature

This paper presents the course of an experiment aimed at verifying the possibility of consolidating a lunar regolith simulant by microwave sintering at the softening temperature of glass. A properly prepared mixture of glass and pumice placed in steel molds inside a hot pot microwave crucible was used as the simulant. The obtained specimens were subjected to macroscopic visual inspection both before and after compressive strength testing. Satisfactory results were obtained, confirming the formulated thesis. At the same time, the need to refine the sintering process in order to obtain samples with the desired reproducible parameters was pointed out.

---

W artykule przedstawiono przebieg eksperymentu, którego celem była weryfikacja możliwości konsolidowania symulantu księżycowego regolitu przez mikrofalowe spiekanie w temperaturze mięknienia szkła. Jako symulant wykorzystano odpowiednio przygotowaną mieszankę szkła i pumeksu umieszczoną w stalowych formach wewnątrz tygla mikrofalowego typu Hot Pot. Uzyskane próbki poddano makroskopowym oględzinom zarówno przed, jak i po przeprowadzeniu badania wytrzymałości na ściskanie. Uzyskano satysfakcjonujące rezultaty potwierdzające sformułowaną tezę. Wskazano jednocześnie na konieczność dopracowania procesu spiekania w celu uzyskiwania próbek o żądanych, powtarzalnych parametrach.