Tribological Properties of Al2O3/ZrO2 Sintered Ceramics
The paper presents mechanical and tribological properties of Al2O3/ZrO2 composite sinters with different proportions of Al2O3 and ZrO2 phases. These materials are commonly used in dry friction contact due to relatively low manufacturing costs of even complex shapes of products and the possibility of working at elevated temperatures. The tests were carried out by the ball-on-disc method at temperatures of 20, 150, 300, and 500°C. A ball made of Al2O3 was used as a counterpart. The results were compared with the following sintered mono-phase materials: Al2O3 (alumina) and tetragonal yttria-stabilized ZrO2 polycrystallines (Y-TZP). The tests showed the significantly better properties of composite materials.
W pracy przedstawiono właściwości mechaniczne i tribologiczne spieków kompozytowych Al2O3/ZrO2 o różnej proporcji faz Al2O3 i ZrO2. Są to materiały chętnie stosowane w węzłach tarcia suchego ze względu na relatywnie niskie koszty wytwarzania nawet skomplikowanych kształtów wyrobów i możliwość pracy w podwyższonych temperaturach. Testy przeprowadzono na stanowisku z węzłem tarcia ball-on-disc w temperaturach 20, 150, 300 i 500°C, jako przeciwpróbkę zastosowano kulkę wykonaną z Al2O3. Wyniki badań porównywano z wynikami badań spieków wytwarzanych z materiałów jednofazowych: α- Al2O3 (korund) i tetragonalnych polikryształów ZrO2 stabilizowanych tlenkiem itru (tzw. Y-TZP). Badania wykazały znacząco lepsze własności materiałów kompozytowych.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).