Mechanical and tribological properties of SBR graphene composites
Hybrid SBR composites have been compounded containing graphene nano-platelets in order to improve technical elastomer performance and to reduce the energy dissipation during frictional processes. It is still unclear how to manage a satisfactory exfoliation and inclusion in a rubber matrix. Therefore, investigations were focused on novel carbon-based nanostructured fillers (graphene nano-platelets) with less than 10 nm thickness. In nearly all cases a significant level of friction reduction was achieved. The resulting stick-slip phenomena and properties were described. Moreover, static gas adsorption, curing, mechanical and dynamic mechanical properties were investigated.
Hybrydowe kompozyty SBR zostały połączone z nanopłytkami grafenu w celu poprawy parametrów technicznych elastomerów i zmniejszenia rozpraszania energii podczas procesów tarcia. Nadal nie jest jasne, jak poradzić sobie z zadowalającą eksfoliacją i wprowadzaniem do matrycy kauczukowej. Dlatego też badania koncentrowały się na nowych nanostrukturalnych napełniaczach węglowych (nanopłytkach grafenowych) o grubości mniejszej niż 10 nm. W prawie wszystkich przypadkach osiągnięto znaczny poziom redukcji tarcia. Opisano wynikające z tego zjawisko stick-slip i właściwości. Ponadto zbadano adsorpcję statyczną gazów, utwardzanie, właściwości mechaniczne i dynamo-mechaniczne.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).