Effect of braze welding parameters on the structure and mechanical properties of joints made of steel CPW 800. Part 1: Arc braze welding
Presently, the reduction of kerb weight consists in the replacement of previously used structural materials with new ones, characterised by more favourable operating parameters. Advantageous mechanical properties of steel elements are primarily obtained through precise hot treatment performed after cold rolling or, in cases of hot-rolled products, through thermo-mechanical treatment. When subjected to welding, the above named materials reveal high sensitivity to intense thermal cycles accompanying welding processes. The article presents the results of technological tests concerning the effect of arc weld brazing on the structural and mechanical properties of joints made of multiphase steel CPW 800.
Redukcja masy własnej wyrobów odbywa jest obecnie poprzez zastępowanie dotychczas stosowanych materiałów konstrukcyjnych nowymi, o większych parametrach użytkowych. Duże właściwości mechaniczne elementów stalowych uzyskiwane są przede wszystkim na drodze precyzyjnej obróbki cieplnej po walcowaniu na zimno lub obróbki cieplno-mechanicznej, w przypadku wyrobów walcowanych na gorąco. Problematyka łączenia tych materiałów za pomocą metod spawalniczych związana jest z ich dużą wrażliwością na ostry cykl cieplny towarzyszący procesom spawalniczym. W artykule przedstawiono wyniki badań technologicznych wpływu procesu lutospawania łukowego na właściwości mechaniczne oraz strukturalne połączeń wielofazowej stali CPW 800.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.
Wersja polska artykułu w wydaniu papierowym s. 23-28.