New self-stratifying adhesives – assessment of stratification degree
New, self-stratifying adhesives composed of epoxy resin and one of selected silane terminated polymers with molecular weights in the range of 10 000–33 000 g/mol were tested. Stratification of the adhesive compositions was assessed on the basis of FTIR spectra and microscopic images of cross sections of the adhesive coatings. It has been found that it is possible to select a resin pair capable of phase separation and migration to the air/coating and coating/substrate interfaces. The best degree of stratification of resins was obtained for a composition containing an STP with the highest molecular weight and viscosity, and the lowest solubility parameter value.
Przebadano nowe, samorozwarstwiające się kompozycje klejowe złożone z żywicy epoksydowej i jednego z wytypowanych polimerów zakończonych grupami silanowymi o masach cząsteczkowych w zakresie 10 000–33 000 g/mol. Rozwarstwienie kompozycji klejowych oceniano na podstawie widm wykonanych techniką FTIR oraz obrazów mikroskopowych przekrojów poprzecznych powłok klejowych. Stwierdzono, że istnieje możliwość dobrania par żywic zdolnych do separacji fazowej i migracji rozdzielonych faz do granicy powietrze/powłoka i powłoka/ podłoże. Najlepszy stopień rozwarstwienia żywic uzyskano w wypadku kompozycji zawierającej polimer STP o największej masie cząsteczkowej i lepkości oraz o najmniejszej wartości parametru rozpuszczalności.
Opracowanie rekordu ze środków MNiSW, umowa nr POPUL/SP/0154/2024/02 w ramach programu "Społeczna odpowiedzialność nauki II" - moduł: Popularyzacja nauki (2025).