Microstructure and microhardness in the area of heat influence zone of HS 6-5-2 steel remelted by a GTAW method

The work presents characteristic microstructures from heat influence zone of HS 6-5-2 high-speed steel remelted with use of GTAW method. Also photos of indentations made by Hanemann microhardness tester attached, which correspond to given microstructures. This work shows that within the area of heat influence zone various processes take place depending on local temperature and steel structure before remelting process. In the area heat influence zone of second remelting overlapping on a first remelting, where temperature was higher than solidus, the eutectic undergone significant transformation. In the area heat influence zone of second remelting overlapping on a steel core structure, a process of carbide phase dissolution occurred, forming of austenite grains, and in areas where temperature was higher than solidus the eutectic mixture was formed on borders of the cells.

---

W pracy przedstawiono charakterystyczne mikrostruktury ze strefy wpływu ciepła stali szybkotnącej HS 6-5-2 nadtopionej metodą GTAW. Zamieszczono również zdjęcia odcisków, wykonanych mikrotwardościomierzem Hanemanna, odpowiadających danym mikrostrukturom. Z pracy wynika, iż w strefie wpływu ciepła zachodzą różne procesy, w zależności od lokalnej temperatury i struktury stali przed nadtopieniem. W obszarze nakładania strefy wpływu ciepła drugiego nadtopienia na strefę pierwszego nadtopienia, i temperatura była wyższa od solidus, wyraźnej przemianie uległa eutektyka. W obszarze nakładania strefy wpływu ciepła drugiego nadtopienia na strukturę rdzenia następował proces rozpuszczania fazy węglikowej, formowania się ziarn austenitu oraz w obszarach gdzie temperatura była wyższa od solidus, dochodziło do powstania eutektyki na granicach komórek.