Possibility of obtaining lanthanum doped nickel coatings from baths based on deep eutectic solvents
Lanthanum-doped nickel coatings were obtained from the bath based on a deep eutectic solvent: choline chloride and propylene glycol, mixed in a molar ratio of 1 : 2, and 0.2 mol dm−3 NiCl2 ∙ 6H2O and 0.5 mol dm−3 LaCl2 ∙ xH2O. The morphology, topography and chemical composition were examined. The lanthanum content in the coating was determined to be 1.7 wt. % using the ICP-MS method. Lanthanum on the surface was mainly in the form of lanthanum carbonate. The obtained coating was exposed to a 7-day exposure in 0.05 mol dm−3 NaCl solution. The coating showed the highest corrosion resistance (Rp ~ 30 kΩ cm2) after 15 hours of exposure to the NaCl solution.
Powłoki niklowe domieszkowane lantanem zostały otrzymane z kąpieli na bazie rozpuszczalnika eutektycznego chlorku choliny i glikolu propylenowego zmieszanych w proporcjach molowych 1 : 2 oraz 0,2 mol dm−3 NiCl2 ∙ 6H2O i 0,5 mol dm−3 LaCl2 ∙ xH2O. Zbadano morfologię, topografię oraz skład chemiczny. Zawartość lantanu w powłoce została określona na 1,7% mas. techniką ICP-MS. Na powierzchni powłoki lantan występował głównie w postaci węglanu lantanu. Otrzymana powłoka została poddana 7-dniowej ekspozycji w 0,05 mol dm−3 roztworze NaCl. Największą odporność na korozję powłoki stwierdzono po 15-godzinnej ekspozycji w roztworze NaCl.
Opracowanie rekordu ze środków MEiN, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2022-2023).