Prediction of Compression Properties of Single Jersey Weft-knitted Fabric by Finite Element Analysis Based on the Hyperfoam Material Model
A 3-D finite element model based on the hyperfoam material model was developed in order to predict the compression behaviour of knitted fabrics in a large deformation state. The degree of compressibility of the fabric is determined by the extent of its volume reduction under external pressure. The compression properties of nine produced knitted fabrics at eight pressure values (2.04, 5.10, 10.19, 20.39, 50.97, 101.94, 152.90, and 203.87 kPa) were measured using a fabric thickness tester and results were compared with finite element results. The FEM results of fabric thickness changes (∆T) and fabric compressibility (EMC) showed good agreement with experimental results, with an average error of 5 and 4.9 percent, respectively. However, the results of fabric linearity of the compression (LC) and work of compression (WC) showed fair agreement, with an average error of 24.5 and 24 percent, respectively.
Publikacja dotyczy analizy kompresji dzianin lewo-prawych o trzech wariantach splotów. Scharakteryzowano parametry dzianin, tj. ścisłości rządkowe i kolumienkowe, masy, zapis splotu w rzeczywistym przebiegu i na igłach. Wykonano badania eksperymentalne i teoretyczne procesu ściskania dzianin wraz z analizą porównawczą. Badania teoretyczne przeprowadzono w ramach eksperymentu numerycznego w środowisku programu ABAQUS. Uzyskane wyniki badań posłużą w projektowaniu właściwości fizycznych wyrobów skarpetkowych przeznaczonych dla diabetyków.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.