Degradation of La2Zr2O7thermal barrier coatings
The degradation process of La2Zr2O7 thermal barrier coatings (TBC) was presented in this paper. This system was deposited by air plasma spraying (APS) on AMS5599 alloy and on a NiCrAlY bond-coat. A scope of tests consisting of isothermal oxidation in air atmosphere at 1100°C for 500 h was performed. Detailed microstructural tests were carried out after 2, 10, 48, 175 and 500 hours of exposure. These tests included microstructure evaluation of a ceramic layer in both coating types, while particularly taking into account phenomena, which occur in a TGO (thermally growth oxide) zone. Evaluation of TGO zone growth was worked out and obtained results were compared with data for conventional TBC layers, which were deposited from 8YSZ powders.
W prezentowanym artykule przedstawiono proces degradacji powłok termoizolacyjnych TBC typu La2Zr2O7 Układ ten został wytworzony metodą natrysku plazmowego (APS) na stopie AMS5599 z międzywarstwą NiCrAlY. Zakres badań obejmował statyczne utlenianie próbek w atmosferze powietrza o temperaturze 1100° C przez 500 godzin. Szczegółowe badania mikrostruktury przeprowadzono po 2, 10, 48, 175 i 500 godzinach ekspozycji. Testy te obejmowały ocenę mikrostruktury warstwy ceramicznej obu typów, ze szczególnym uwzględnieniem zjawisk zachodzących w strefie TGO. Dokonano oceny wzrostu strefy TGO, a uzyskane wyniki porównano z danymi dla konwencjonalnych warstw TBC, które zostały osadzone z proszków 8YSZ.
This work was supported by the National Science Centre, Poland under grant number 2016/21/D/ST8/01687.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).