Effect of shells number and machining on selected properties of 3D-printed PLA samples
Effect of shells number (1–5) on tensile properties of PLA samples printed using the FDM/FFF technique was investigated. The crack surface was also analyzed. The best properties were obtained for 4-shell sample. However, due to the large coefficient of variation (>> 10%) in the case of elongation, 3-shell sample was selected for testing the machining impact. Such a large coefficient of variation can be explained by the presence of voids between the layers. The greater the number of layers, the greater the structure defects. Machining increases surface smoothness while reducing tensile strength and practi¬cally unchanged elongation at break.
Zbadano wpływ liczby warstw (1–5) na właściwości mechaniczne przy rozciąganiu próbek PLA otrzymanych techniką FDM/FFF. Analizie poddano także powierzchnie pęknięć. Najlepsze właściwości uzyskano dla próbki 4-warstwowej. Jednak, ze względu na duży współczynnik zmienności (>> 10%) w przypadku wydłużenia, do badań wpływu obróbki skrawaniem wytypowano próbkę 3-warstwową. Tak duży współczynnik zmienności można wyjaśnić obecnością pustych przestrzeni pomiędzy warstwami. Im większa liczba warstw, tym większe defekty struktury. Obróbka skrawaniem zwiększa gładkość powierzchni przy jednoczesnym zmniejszeniu wytrzymałości na rozciąganie i praktycznie niezmienionym wydłużeniu przy zerwaniu.
Opracowanie rekordu ze środków MNiSW, umowa nr POPUL/SP/0154/2024/02 w ramach programu "Społeczna odpowiedzialność nauki II" - moduł: Popularyzacja nauki (2025).