Electrical double layer at manganese oxides/1:1 electrolyte solution interface

Results of the investigations of the electrical double layer (edl) at manganese oxides/ aqueous solution of alkali metal chlorides interface are presented. The solid phase in the experiments consists of Mn2O3 or MnO2. Dzeta potential ( ) and surface charge (?0) measurements for the mentioned oxides were performed in 0.1- 0.001M solutions of LiCl, NaCl and CsCl. On the basis of surface charge density as a function of pH and ionic strength data the ionization and complexation constants of surface hydroxyl groups were calculated. The surface charge measurements and cation adsorption data indicated that the sequence of the adsorption of alkali metal cations is Li> Na>Cs.

---

Przedstawiono wyniki badań podwójnej warstwy elektrycznej na granicy faz tlenki manganu/wodny roztwór chlorków metali alkalicznych. Badania prowadzono nad właściwościami granicy faz w których fazę stałą stanowiły tlenki manganu; Mn2O3 i MnO2. Pomiary . i ładunku powierzchniowego (.0) dla wyżej wymienionych tlenków przeprowadzono w 0.1-0.001M roztworach LiCl, NaCl, CsCl. W oparciu o zależności gęstości ładunku powierzchniowego, potencjału . od pH i stężenia elektrolitu obliczono stałe jonizacji i kompleksowania powierzchniowych grup hydroksylowych tlenków. Na podstawie pomiarów ładunku powierzchniowego oraz przez bezpośredni pomiar adsorpcji kationów określono następująca sekwencję adsorpcji kationów Li>Na>Cs.