The impact of flow induced changes of polymers density on rheological measurements

The influence of real density of polymers in molten state on the rheological values is presented. The investigations were performed by means of extrusion rheometer, using a rheological dye with exchangeable channel with various length and diameter ratio (L/D). The materials used in the experiments were low density polyethylene (PE-LD), middle density polyethylene (PE-MD) and the blend of PE-LD with PE-MD in 1:1 ratio, for which p-v-T diagrams were determined. Based on p-v-T measurements the real specific volume and the density of the molten polymer in defined processing conditions (p, T), were found (Fig. 4). Density was used for determination of the real mass flow ratio Q. A significant influence of the channel L/D ratio on changes of density was stated (Fig. 5, Table 1). The dependence of changes of density values on the type of polymer used was confirmed.

---

Pomiary przeprowadzono za pomocą reometru wytłaczarkowego używając dysz cylindrycznych o przekroju kołowym z różnym stosunkiem długości do średnicy (L/D). Badano polietylen małej gęstości (PE-LD), polietylen średniej gęstości (PE-MD) oraz ich mieszaninę w stosunku 1:1 wyznaczając diagramy p-v-T. Na podstawie wykresów p-v-T określano objętość właściwą, a następnie gęstość (&ro;) polimeru, w warunkach ciśnienia i temperatury (p, T) odpowiadającym wartościom tych parametrów podczas pomiarów reologicznych (rys. 4). To umożliwiło ocenę rzeczywistej wartości objętościowego natężenia przepływu Q. W przeprowadzonych badaniach wykazano istotny wpływ charakterystycznych wielkości kanału dyszy pomiarowej (L i D) na zmiany gęstości polimeru (rys. 5, tabela 1). Potwierdzono również zróżnicowanie &ro;, w takich samych warunkach przetwórczych, dla różnego typu polietylenu.