Magnetic properties of Fe60 Co 5 Zr 10 Mo 5 B 20 bulk amorphous and partially crystallized soft magnetic alloy

Study of the microstructure and magnetic properties of Fe60Co5Zr10Mo5B20 alloy as a massive plates and rods were performed. The samples were obtained by suction of a liquid alloy onto water-cooled copper mould. From the microstructure investigation it was found that samples obtained as a plates in contrast to rods have full amorphous microstructure. Samples as a rods were partially crystallized. The magnetic measurements performed on hysteresisgrapher (Ferrotester) and vibrating sample magnetometer (VSM) shown that rods have better soft magnetic properties (low coercivity field, high initial permability and saturation of the magnetization) and lesser hysteresis losses. The DSC curves were used to determine thermodynamics of measured alloys. Better thermal stability was obtained for samples in the form of plates.

---

Badania mikrostruktury i właściwości wytworzonych litych stopów magnetycznych Fe60Co5Zr10Mo5B20 w postaci płytek i prętów. Badane próbki zostały wytworzone przez zassanie płynnych stopów do formy miedzianej chłodzonej wodą. Z badań mikrostruktury wynika, że próbki wytwarzane w formie płytek mają strukturę całkowicie amorficzną w przeciwieństwie do prętów, które mają strukturę częściowo krystaliczną. Pomiary magnetyczne wykonane za pomocą histerezografu i magnetometru (VSM) dowiodły, że pręty są bardziej miękkie magnetycznie (posiadają niższe pole, wyższą początkową przenikalność i nasycalność magnetyczną) i mniejsze straty histerezy. Wykresy DTS zostały zastosowane do wyznaczenia termodynamiki badanych stopów. Lepsza stabilność temperaturowa została otrzymana dla próbek w formie płytek.