Producing and properties of the polylactide-alumina nanocomposite fibres

We have described a method of producing polylactide-alumina nanocomposite fibres. Alumina nanoparticles have been combined with polylactide (PLA) to obtain composite. In the next step nanocomposite fibres have been produced by electrospinning method. Nanoalumina has been acquired by an innovative thermal decomposition method, which has been described by us earlier. The morphology and properties of the Al2O3 nanopowder as well as final product were examined using scanning electron microscope (SEM) and BET surface area measurements. Phase composition of the Al2O3 nanopowder was investigated using X-ray diffraction method. Electrospinning method allows producing homogeneous fibres of the nanocomposite PLA-Al2O3. The average particle size of the Al2O3 nanopowder incorporated in fibres was 57.9 nm. Specific BET surface area of the nanoalumina was 289.7 m2.g-1.

---

Opisano metodę produkcji włókien nanokompozytu polilaktyd-tlenek glinu. Nanocząstki tlenku glinu połączone zostały z polilaktydem (PLA), a następnie z otrzymanego kompozytu wytworzono włókna metodą electrospinning'u. Nanotlenek glinu otrzymany został, opisaną przez autorów wcześniej, nowatorską metodą rozkładu termicznego. Morfologia i właściwości nanoproszku Al2O3, podobnie jak i produktu finalnego, przeanalizowane zostały za pomocą skaningowego mikroskopu elektronowego (SEM) oraz pomiarów powierzchni właściwej metodą BET. Skład fazowy nanoproszku Al2O3 zbadany został za pomocą dyfraktometru rentgenowskiego. Metoda electrospinning'u pozwala na wyprodukowanie homogenicznych włókien nanokompozytu PLA-Al2O3. Średnia wielkość cząstki nanoproszku Al2O3 wprowadzonego do włókien wyniosła 57,9 nm. Powierzchnia właściwa nanotlenku glinu wyniosła 289,7 m2.g-1.