The influence of chemical intercalation of graphite fibers with H2SO4/CrO3 system on the successive electrochemical intercalation of sulphuric acid

Electrochemical intercalation of 18 M sulphuric acid into graphite fibers Thornell K-l 100 and the original and intercalated VGCFs was examined. It is shown that the successive intercalation of sulphuric acid into VGCFs modified with H-,SO4 and/or CrO3 depends on the properties of the original compound resulting from the method of intercalation. A very interesting feature is the fact that the cyclic reversibility of the deinterca-lation/intercalation process for VGCFs improves in the following cycles, and in the third cycle achieves the same value as in case of fibers Thornell K-l 100. The presence of primary intercalate (CrO3 and H2SO4) between the interlayer spacings of fibers VGCFs facilitates the successive electrochemical intercalation of sulphuric acid and gives rise to the increase of the cyclic reversibility of the deintercalation/intercalation process. It is shown that both the original and intercalated VGCFs undergo overoxidation.

---

Badano elektrochemiczną interkaiację kwasu siarkowego w włókna grafitowe Thornell K-1100 oraz w czyste i interkalowane włókna VGCFs. Pokazano, że interkalacja kwasu siarkowego w modyfikowane H2SO4 i/lub CrO3 włókna VGCFs zależy od właściwości związku wynikających z metody interkalacji. Bardzo interesujący jest fakt, że cykliczna odwracalność procesu deinterkalacji/interkalacji dla VGCFs poprawia się w kolejnych cyklach i w trzecim cyklu osiąga taką samą wartość jak w przypadku włókien Thornell K-1100. Obecność pierwotnego interka-latu (CrO3 i H2SO4) w przestrzeniach międzywarstwowych włókien VGCFs ułatwia elektrochemiczną interkalację kwasu siarkowego i powoduje wzrost cyklicznej odwracalności procesu deinterkalacji/interkalacji. Pokazano, że zarówno czyste jak i interkalowane włókna VGCFs ulegają przetlenieniu.