Mechanical properties and resistance to oxidation tests of cable polyethylene modified with plasma carbon black

The new kind of cable polyethylene was produced by modification with plasma carbon black, which can be use as an antioxidant and pigment. The paper presents mechanical and oxidation induction time tests of cable polyethylene modified with changeable content of plasma carbon black from 0.1 % to 1.0 wt. %. The mechanical tests enclose Brinell-Vickers hardness number, melt flow rate and static tensile strength. The results showed the increased oxidation induction time, 57 min, for 0.5 wt. % of plasma carbon black in the composition. The results were compared with those concerning commercial cable polyethylene modified by furnace carbon black.

---

Przedstawiona odmiana polietylenu kablowego została wytworzona w wyniku modyfikacji plazmową sadzą techniczną, która jest stosowana jako przeciwutleniacz i pigment. Scharakteryzowano strukturę i właściwości adsorpcyjne użytej sadzy plazmowej (rys. 1 i 2, tabela 1). Zbadano właściwości mechaniczne (twardość metodą Brinella-Vickersa, wskaźnik szybkości płynięcia, statyczną wytrzymałość na rozciąganie, wydłużenie) oraz odporność na utlenianie polietylenu kablowego modyfikowanego zmienną ilością (0,1-1,0 % mas.) tej sadzy (tabela 2, rys. 3). Największe wartości czasu indukcji utleniania (OIT) w połączeniu z najlepszymi właściwościami mechanicznymi uzyskano w przypadku próbki zawierającej 0,5 % mas. plazmowej sadzy technicznej. Właściwości badanych kompozycji porównano z właściwościami handlowego polietylenu kablowego modyfikowanego piecową sadzą techniczną (PE LE6022 w tabeli 2).