Oxidation of VOCs over monolithic perovskite catalysts.

Three monolithic perovskite catalysts, one bulk LH and two WK-coated on cordierite support, and one basing on Cu-Co-Mn oxides on cordierite monolith, were manufactured. They were tested for oxidation of selected hydrocarbons (toluene, n-hexane) and oxyderivatives (acetone, Et acetate, Bu acetate). LaMnO3 perovskite was used as active phase in preparation of WK catalysts, with La3+ ions partially exchanged for Ag+ ions (25 and 50%). Hydrocarbons were oxidized with lower efficiency than oxyderivatives, but they underwent oxidation to CO2 and water over all catalysts investigated. Oxidation of oxyderivatives ran via intermediates, first aldehydes, typical products of incomplete oxidation. The concentration of yielded intermediates decreased with the reaction temperature. The addition of silver enhanced catalytic activity and improved reaction selectivity with respect to CO2 and water.

---

Wytworzono trzy monolityczne katalizatory perowskitowe, jeden masowy LH oraz WK na nośniku kordierytowym, oraz jeden na bazie tlenków Cu-Co-Mn, które również naniesiono na monolit kordierytowy. Aktywność katalizatorów określono na podstawie wydajności katalizowanejprzez nie reakcji utleniania wytypowanych węglowodorów (toulenu i n-heksanu) oraz połączeń tlenopochodnych (acetonu, octanu etylu, i octanu butylu). Katalizatory WK wytworzono na bazie perowskitu LaMnO3, w którym atomy lantanu częściowo zastąpiono atomami srebra (w 25 i 50%). Na wszystkich katalizatorach węglowodory utleniały się z mniejszą wydajnością niż połączenia tlenowe, ale produktami reakcji były CO2 i woda. Połączenia tlenowe utleniały się z wytworzeniem produktów pośrednich, głównie aldehydów, typowych produktów niepełnego spalania. Stężenia tych produktów malały ze wzrostem temperatury reakcji. Dodatek srebra zwiększał aktywność katalizatorów i poprawiał selektywność reakcji względem CO2 i wody.