Stability of second phase particles during processing by hydrostatic extrusion

In the present work, the stability of second phase particles in an aluminium alloy during the processing by hydrostatic extrusion and their effect on the process of grain refinement have been investigated. Two types of intermetallics: primary particles and secondary precipitates have been taken into account. The results have shown that the processing by hydrostatic extrusion affects both types of them. The secondary plate-like precipitates transform into spherical particles. Primary particles decrease slightly their size, change their shape into more regular and become more uniformly distributed in the matrix. Intermetallics of both types affect also the process of grain refinement which is favoured by the presence of large primary intermetallics whereas delayed by small precipitates.

---

W niniejszej pracy analizowano stabilność cząstek drugiej fazy w stopach aluminium podczas kształtowania metodą wyciskania hydrostatycznego. Analizę przeprowadzono dla dwóch rodzajów cząstek: (1) pierwotnych cząstek faz międzymetalicznych oraz (2) wtórnych wydzieleń faz międzymetalicznych. Uzyskane wyniki pozwoliły ustalić, że proces wyciskania hydrostatycznego powoduje rozdrobnienie i zmianę kształtu wydzieleń z płytkowego na sferoidalny. Wykazano także, że pierwotne cząstki faz międzymetalicznych podczas procesów wyciskania hydrostatycznego nieznacznie zmniejszają swoje rozmiary, ich kształt staje się bardziej regularny, a rozmieszczenie bardziej jednorodne. Określono także wpływ tych cząstek na proces rozdrobnienia ziarna. Stwierdzono, że duże cząstki pierwotnych faz międzymetalicznych sprzyjają procesowi rozdrobnienia ziarna, natomiast wtórne wydzielenia opózniają ten proces.