Electrical conductivity and corresponding specific eEnergy consumption of new MgO-containing ESR-slags

Continuously increasing product requirements place constant demands on steel manufacturers with regard to innovation. Among them is the development of new Electro Slag Re-melting (ESR) slag concepts, where MgO is one of the basic components. The specific electrical conductivity of CaF2-based MgO-containing ESR slags is determined by a specially constructed measurement cell equipped with four electrodes. The analysed slags are composed either of CaF2-MgO with a maximum content of 15%MgO or of CaF2– 15%CaO with stepwise substitution of CaO by MgO. The results show that the conductivity decreases with rising MgO content. In order to provide a better evaluation of the effects of adding MgO, the results are compared to the specific conductivity of pure CaF2 and a CaF2-CaO-Al2O3 standard slag. The applicability of the laboratory results in industry was verified by re-melting experiments in an electro slag re-melting furnace.

---

Ciągle zwiększające się wymagania, co do jakości produktów, przyczyniają się do stałych nacisków na producentów w zakresie stosowania innowacji. Wśród nich jest rozwój nowej koncepcji żużli EŻP, gdzie MgO jest głównym składnikiem. Przewodność właściwa żużli zawierających MgO, opartych o CaF2, w procesie elektrożużlowego przetapiania jest określo- na przez specjalnie skonstruowany układ pomiarowy wyposażony w cztery elektrody. Analizowane żużle składają się albo z CaF2-MgO z maksymalną zawartością MgO wynoszącą 15%, albo z CaF2- 15%CaO, poprzez stopniowe zastąpienie CaO przez MgO. Wyniki wskazują, że przewodność maleje ze wzrostem zawartości MgO. W celu dostarczenia lepszej oceny efektów dodawania MgO, wyniki zostały porównane z przewodnością czystego CaF2 i standardowych żużli CaF2-CaO-Al2O3. Przydatność wyników laboratoryjnych w przemyśle została zweryfikowana przez próby przetapiania w piecu EŻP.