Characterization of oxide layers made on aluminum alloy 7075 by different methods
Aluminum and aluminum alloys are now being widely used as materials for structural applications due to a number of valuable properties. Improvement in the functional and decorative properties of aluminum can be obtained by forming an oxide layer on its surface. The aim of the present study was to produce and compare the properties of oxide layers on the surface of aluminum alloy 7075 and compare their properties. The methods that were used during the study were as follows: phosphating, micro-arc oxidation, and a chemical method involving the formation of a passive layer. The layers were subjected to corrosion tests. SEM and EDS methods were used for characterization of the received results. Also, some tests on an optical profilometer were done. It was proven that the micro-arc oxidation method allowed us to obtain a layer with the greatest thickness and highest corrosion resistance.
Glin i jego stopy są obecnie powszechnie wykorzystywanym materiałem do zastosowań konstrukcyjnych ze względu stosunek masy do wytrzymałości. Poprawę własności funkcyjnych i dekoracyjnych aluminium uzyskać można przez wytworzenie warstwy tlenku na jego powierzchni. Celem badań było wytworzenie warstw tlenkowych na podłożu ze stopu aluminium 7075 i porównanie ich właściwości. Zastosowano trzy metody: fosforanowanie, micro-arc oxidation oraz metodę chemiczną polegającą na wytworzeniu warstwy pasywnej. Otrzymane powłoki poddano testom korozyjnym oraz charakteryzowano z zastosowaniem następujących metod: SEM, EDS. Wykonano też badania na profilometrze optycznym. Metoda micro-arc oxidation pozwala na uzyskanie warstwy o największej grubości oraz najlepszej odporności na korozję.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).