Influence of the ester block polymerization degree on the structure and properties of ester-ether-amide block terpolymers
New multi-block thermoplastic elastomers (TPEEA) were obtained, consisting of a crystalline amide block (domains), an amorphous ether block (continuous phase) and an ester block with a variable degree of polymerization, which acts as a compatibilizer. The presence of large interfacial areas was observed. It was found that ester blocks with a molecular weight <600 g/mol mix with other blocks, modifying the phases that constitute them and stabilizing the micro- and nanophase structure of the entire system. Short ester blocks act as nucleation precursors, and in the hard phase they have plasticizing properties.
Otrzymano nowe wieloblokowe elastomery termoplastyczne (TPEEA), składające się z krystalicznego bloku amidowego (domeny), amorficznego bloku eterowego (faza ciągła) oraz bloku estrowego o zmiennym stopniu polimeryzacji, który pełni funkcję kompatybilizatora. Zaobserwowano obecność dużych obszarów międzyfazowych. Stwierdzono, że bloki estrowe o masie cząsteczkowej <600 g/mol mieszają się z innymi blokami, modyfikując tworzące je fazy i stabilizując strukturę mikro- i nanofazową całego układu. Krótkie bloki estrowe pełnią funkcję prekursorów zarodkowania, a w fazie twardej mają właściwości uplastyczniające.
Opracowanie rekordu ze środków MNiSW, umowa nr POPUL/SP/0154/2024/02 w ramach programu "Społeczna odpowiedzialność nauki II" - moduł: Popularyzacja nauki (2025).