Evolution of zinc coatings during drawing process of steel wires

The paper shows a significant influence of the multi-stage wire drawing technology on deformability and phase transformations in the zinc coating. SEM tests proved that the coating after hot-dip galvanizing consists of a number of thin layers, ranging from 1 to 5 μm, and differing in thickness, chemical composition and properties. When pulled through the drawing die the zinc coating heats up (as a result of friction between the material and the tool) and its dynamic plastic deformation. It resulted in the fracture and partial crushing of the hard-intermetallic phases. It has been proven that as the wire passes through successive drawing dies, the coating is thinned and diffusion as well as phase remodelling of individual structural components occurs; in the place of phase ζ, the intermetallic phase δ1 develops, increasing its share in the diffusion layer. The crystals of intermetallic phases located on the border of the diffusion and outer layers break up and remain dispersed in the zinc. An analysis of the microhardness of the coating has proven that the level of the increase in the microhardness of the zinc coating is contingent on percentage of iron in particular layers of coating.

---

Opracowanie rekordu ze środków MNiSW, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2024).