Graphene oxide-modified cellulose acetate membranes with improved Congo red removal efficiency
The casting method was used to obtain membranes from cellulose acetate (CA) with different contents (0.1; 0.4; 0.8 wt%) of graphene oxide (GO). FESEM and FT-IR were used to evaluate the membrane structure. The contact angle was also examined. Congo red was used to evaluate the membrane efficiency. The contact angle of CA/GO membranes decreased from 55.47° (CA) to 38.16° (0.4 wt% GO), which indicates good dispersion of GO in the CA matrix. CA/GO membranes showed less irreversible fouling, which indicates that reversible fouling predominated over fouling of all membranes. Increasing the membrane porosity, pore size and hydrophilicity results in higher permeability.
Metodą odlewania otrzymano z octanu celulozy (CA) membrany różniące się zawartością (0,1; 0,4; 0,8% mas.) tlenku grafenu (GO). Do oceny struktury membran zastosowano FESEM i FT-IR. Zbadano również kąt zwilżania. Czerwieni Kongo użyto do oceny wydajności membrany. Kąt zwilżania membran CA/GO zmniejszył się z 55,47° (CA) do 38,16° (0.4% mas. GO), co świadczy o dobrej dyspersji GO w osnowie CA. Membrany CA/GO wykazywały mniejsze nieodwracalne zanieczyszczenie, co wskazuje, że odwracalne zanieczyszczenie przeważało nad zanieczyszczeniem wszystkich membran. Zwiększenie porowatości membran, wielkości porów i ich hydrofilowości skutkuje większą przepuszczalnością.
Opracowanie rekordu ze środków MNiSW, umowa nr POPUL/SP/0154/2024/02 w ramach programu "Społeczna odpowiedzialność nauki II" - moduł: Popularyzacja nauki (2025).