Comparison of the structure and mechanical properties of coatings arc-sprayed with EuTronic Arc flux-cored wires

The article compares the erosion resistance, roughness and hardness of coatings produced by arc spraying. The study was conducted to compare the properties of arc-sprayed coatings with EuTronic Arc 599 and EuTronic Arc 595 powder wires on ASTM A516 Gr. 55 unalloyed steel substrates. Tests showed that the EuTronic Arc coatings exhibited very high hardness, averaging 755 HV for the EuTronic Arc 595 coating and 821 HV for the Eutronic Arc 599 coating. Application of the coatings increased the hardness, relative to the parent material, by 360 % and 400 %, respectively. The EuTronic Arc 599 coating showed a significantly higher roughness averaging 16.12 μm, compared to 12.35 μm for the EuTronic Arc 595 coating, which was likely caused by greater plasticization of the material during spraying resulting from the absence of carbides.

---

Artykuł zawiera porównanie odporności erozyjnej, chropowatości oraz twardości powłok wytwarzanych metodą natryskiwania łukowego. Przeprowadzone badania miały na celu porównanie właściwości powłok natryskiwanych łukowo drutami proszkowymi EuTronic Arc 599 oraz EuTronic Arc 595 na podłoże ze stali niestopowej ASTM A516 Gr. 55. Badania potwierdziły, że powłoki EuTronic Arc wykazują bardzo wysoką twardość, wynoszącą średnio 755 HV dla powłoki EuTronic Arc 595 oraz 821 HV dla powłoki Eutronic Arc 599. Naniesienie powłok podwyższyło twardość, w stosunku do materiału rodzimego, odpowiednio o 360 % oraz 400 %. Powłoka EuTronic Arc 599 wykazała znacznie wyższą chropowatość, wynoszącą średnio 16,12 μm, w stosunku do 12,35 μm dla powłoki EuTronic Arc 595, co prawdopodobnie zostało spowodowane większym uplastycznieniem materiału podczas natryskiwania, wynikającym z braku obecności węglików.