The influence of low temperature glow discharge assisted nitriding on corrosion resistance of NiTi shape memory alloy

NiTi shape memory alloys are used for bone and cardiological implants. However, on account of metalosis effect, i.e. the migration of the alloy constituents into the surrounding tissues, they are submitted to various surface treatment processes in order to improve their corrosion resistance. In this article, comparative study of NiTi alloys corrosion resistance both after the process of nitriding in low-temperature plasma at the temperature of 300°C (which guarantees preservation of their favourable functional properties) and without submitting them to this process is presented. Examinations with the use ofpotentiodynamic and impedance spectroscopy methods were made which show an increase of corrosion resistance after the glow discharge assisted nitriding. Corrosion resistance tests were supplemented by morphology and roughness tests of NiTi alloy surface both with diffusive layer and without it.

---

Stopy z pamięcią kształtu NiTi stosowane są na implanty kostne i kardiologiczne. Ze względu jednak na zjawisko metalozy, tj. przechodzenia składników stopu do otaczających tkanek, są poddawane różnym obróbkom powierzchniowym w celu poprawy ich odporności na korozję. W artykule przedstawiono badania porównawcze odporności na korozję stopów NiTi bez i po procesie azotowania w niskotemperaturowej plazmie w temperaturze 300°C, tj. gwarantującej zachowanie ich korzystnych właściwości użytkowych. Przeprowadzono badania metodą potencjodynamiczną i spektroskopii impedancyjnej, wykazując wzrost odporności korozyjnej tych stopów po procesie azotowania jarzeniowego. Jako uzupełnienie badań korozyjnych zrealizowano również badania morfologii oraz chropowatości powierzchni stopu NiTi bez i z wytworzoną warstwą dyfuzyjną.