Influence of the chemical composition on the hardness of defibrator plate segments
Influence of the chemical composition on the hardness of defibrator plate segments. The paper presents the results of the hardness measurements of the material of defibrator plate segments, in connection with their chemical composition. The investigations of the chemical composition were performed using Energy Dispersive X-ray Spectroscopy (EDS). The hardness was measured using the Rockwell method. The increased number of the alloy components leads to an increase in hardness by approx. 3%, in comparison with the normalized L210H21S cast steel. Changes of the chemical composition and increase in the number of alloy components are ineffective from the viewpoint of the alloy hardness.
Wpływ składu chemicznego na twardość segmentów tarcz mielących termorozwłókniarki. W artykule przedstawiono wyniki pomiarów twardości materiału segmentów tarcz mielących termorozwłókniarki w powiązaniu z badaniami jego składu chemicznego. Badania składu chemicznego były prowadzone metodą Rentgenowskiej Spektroskopii Dyspersji Energii. Twardość była mierzona metodą Rockwella. Zwiększanie liczby dodatków stopowych, w porównaniu ze znormalizowanym staliwem L210H21S, powoduje wzrost twardości o ok. 3%. Zmiana składu chemicznego i zwiększanie liczby dodatków stopowych są nieefektywne z punktu widzenia twardości.
Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2021).