Laser welding of high-strength steel S960QL
The article discusses the results of tests concerning the effect of parameters used during the basic bead-on-plate laser welding (i.e. location of the laser beam focus, welding rate and linear welding energy) of 4.0 mm thick sheets made of high-strength steel S960QL on the quality and properties of simulated butt joints. The welding tests were performed using a YAG TruDisk 3302 Yb disk laser (TRUMPF) having a maximum output power of 3.3 kW and provided with a head focusing the laser beam spot to a diameter of 200 μm. The simulated butt welded joints were made without the filler metal, using a technique which consisted in the laser beam melting of sheets. Macroscopic and microscopic tests as well as impact strength tests, fractographic tests and microhardness measurements involved the cross-section of the simulated specimens.
W artykule opisano wyniki badań wpływu podstawowych parametrów spawania laserowego (tj. położenia ogniska wiązki laserowej, prędkości spawania oraz energii liniowej spawania) blach o grubości 4,0 mm ze stali o wysokiej wytrzymałości S960QL na jakość i właściwości symulowanych złączy doczołowych. Próby spawania wykonano za pomocą lasera dyskowego Yb:YAG TruDisk 3302 firmy TRUMPF o mocy maksymalnej 3,3 kW z głowicą ogniskującą wiązkę do średnicy 200 μm. Symulowane złącza doczołowe blach spawano bez materiału dodatkowego techniką polegającą na przetapianiu blach wiązką laserową. Wykonano badania makro- i mikroskopowe, próby udarności, badania fraktograficzne oraz pomiary mikrotwardości na przekroju poprzecznym próbek.
Opracowanie rekordu ze środków MEiN, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2022-2023).