Ultrasonic Tests of FSW Joints of Thicknesses below 8 mm
The article presents results of ultrasonic tests concerning 6 mm thick FSW joints made of aluminium grade 2017. The tests were performed using joints with artificial post-weld welding imperfections and joints characterised by internal imperfections. The test results revealed that the use of the ultrasonic technique enabled assessments of the quality of 6 mm FSW joints. However, it should be noted that the characteristic geometry of welded joints made using the abovenamed method is responsible for the fact that an ultrasonic wave undergoes transformation, reflection and damping after entering a tested object. In addition, it is necessary to use specialist tandem-type probes applied when testing thin-walled elements.
Przestawiono wyniki badań ultradźwiękowych złączy zgrzewanych metodą FSW o grubości 6 mm wykonanych ze stopu aluminium w gat. 2017. Badania były przeprowadzone na złączach ze sztucznie wprowadzonymi niezgodnościami po procesie zgrzewania oraz na złączach charakteryzujących się niezgodnościami wewnętrznymi. Na podstawie otrzymanych wyników można stwierdzić, że przy użyciu techniki ultradźwiękowej można oceniać jakość złączy zgrzewanych metodą FSW o grubości 6 mm. Należy jednak zaznaczyć, iż charakterystyczna geometria złączy zgrzewanych tą metodą powoduje, że wprowadzana fala ultradźwiękowa ulega zjawiskom transformacji, odbiciu i tłumieniu. Ponadto niezbędnym jest zastosowanie specjalistycznych głowic typu tandem, które są przeznaczone do badania elementów cienkościennych.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).