Influence of matrix structure on fatigue properties of nodular cast iron

Sixteen heats of unalloyed and alloyed nodular cast iron were thermally treated in different ways and 34 materials were obtained with ferritic, ferritic-pearlitic and pearlitic structures and with structures of upper, transition and lower bainite. For all those materials static and fatigue tests were made - the latter mostly in symmertical tension-compression loading but some of them also in repeated tension and pulsating bending. From results of fatigue tests the fatigue limits for 10'7 cycles were determined and some Haigh diagrams were drawn. Special care was given to the study of the dependence between tensile strength and fatigue limit.

---

Z szesnastu wytopów niestopowego i stopowego żeliwa sferoidalnego, przy pomocy różnych rodzajów obróbki cieplnej uzyskano 34 gatunki żeliwa ze strukturą: ferrytyczną, ferrytyczno-perlityczną i perlityczną oraz ze strukturą górnego, przejściowego i dolnego banitu. Dla wszystkich otryzemanych gatunków zostały wykonane badania statyczne i zmęczeniowe. Większość badań zmęczeniowych przeprowadzono przy symetrycznym obciążeniu rozciągającym i ściskającym, a także niektóre z nich przy rozciąganiu tętniącym i zginaniu pulsującym. Wyniki badań zmęczeniowych przedstwiono na wykresach Haigha. W analizie wyników badań szczególną uwagę zwrócono na zalaeżność między wytrzymałością na rozciąganie a granicą zmęczeniową żeliwa sferoidalnego.