Influence of precipitation strenghtening process on tensile and fracture behaviour of the 6005 and 6082 alloys

The main task of this work was to study the effect of the precipitation hardening on the mechanical properties and fracture toughness of 6005 and 6082 aluminium alloys. The mechanical (Rm and Rp0,2) and plastic (A) properties of the examined alloys were evaluated by uniaxial tensile test at room temperature. Additionally the artificially aged alloys have been tested in tension in order to determine its fracture toughness. Thus, standard ASTM tests were performed on fatigue precracked compact tension (KIC) and sharp-notched specimens (Rm sup k) in both the longitudinal and transverse orientation with respect to the rolling direction. The results show that the microstructure, mechanical properties and fracture toughness changes during artificial aging due to the precipitation strengthening process.

---

W pracy podjęto badania celem określenia oddziaływania warunków prowadzenia procesu umacniania wydzieleniowego na właściwości mechaniczne oraz odporność na pękanie stopów aluminium 6005 i 6082. Właściwości mechaniczne (Rm i Rp0,2) i plastyczne (A) wyznaczono w próbie statycznej rozciągania w temperaturze pokojowej. W celu określenia odporności na pękanie stopów umocnionych wydzieleniowo przeprowadzono próby rozciągania próbek kompaktowych (KIC) oraz z ostrym karbem (Rm ig k) wyciętych zgodnie z kierunkiem największego odkształcenia plastycznego w kierunku do niego prostopadłym. Na podstawie otrzymanych wyników stwierdzono, że decydujący wpływ na zmianę mikrostruktury, właściwości mechanicznych oraz odporności na pękanie mają warunki prowadzonego procesu umacniania wydzieleniowego.