Influence of methodical factors on results of a quantitative evaluation of y' phase in MAR M247 superalloy

The nickel-based superalloy MAR M247 is precipitation strengthened by coherent with matrix y' precipitates. The superalloy was investigated by means of scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The scanning electron microscopy images were used for a stereological evaluation of the y' precipitates size and shape, density and volume fraction distributions. In the work several examples of y' phase primary precipitates quantitative evaluation conducted on the same sample after y' phase revealing by various methods were presented. The analysis was carried out on microstructures images registered using secondary electrons (SE) technique by means of image analysis software.

---

Nadstop na osnowie niklu MAR M247 jest umacniany wydzieleniowo koherentnymi z osnową wydzieleniami y'. Poddano go badaniom z wykorzystaniem elektronowej mikroskopii skaningowej (SEM) i transmisyjnej (TEM). Obrazy z elektronowego mikroskopu skaningowego poddano ocenie stereologicznej pod kątem oceny rozkładów wielkości i kształtu, gęstości i udziału objętościowego wydzieleń y'. W pracy przedstawiono kilka przykładów oceny ilościowej pierwotnych wydzieleń fazy y' przeprowadzonej na tej samej próbce po ujawnieniu fazy y' różnymi metodami. Analizę przeprowadzono na obrazach mikrostruktury zarejestrowanych techniką elektronów wtórnych (SE) za pomocą programu do analizy obrazu.