An effect of annealing on electric properties of nanocomposites (CoFeZr)x(Al2O3)1-x produced by magnetron sputtering in the atmosphere of argon and oxygen beyond the percolation threshold

The paper presents results of real part AC conductivity dependences on alternating current frequency, measuring temperature and annealing temperature in (CoFeZr)x(Al2O3)1-x nanocomposite sample beyond the percolation threshold deposited in argon and oxygen mixed gas ambient. It has been found that at the annealing temperature of 698 K and higher the additional oxidation of metallic “core/shell”-like nanoparticles occurs resulting in transition from conductivity with ó(f)=const to hopping regime with ó(f)~f á. Using the developed electron hopping model we have extracted the mean electron hopping length r1 = 2.6 nm from experimental results for annealed nanocomposite sample.

---

W artykule zaprezentowano wyniki bada. zale.no.ci konduktywno.ci probki nanokompozytu (CoFeZr)x(Al2O3)1-x wytworzonej w otoczeniu mieszaniny argonu i tlenu od cz.stotliwo.ci pr.du zmiennego, temperatury pomiarowej i temperatury wygrzewania poza progiem perkolacji. Stwierdzono, .e przy temperaturach wygrzewania 698 K i wy.szych zachodzi dodatkowe utlenianie powierzchni nanocz.steczek fazy metalicznej jako efekt przej.cia od przewodno.ci z �Đ(f)=const do przewodo.ci skokowej z �Đ(f)~f �ż. Przy u.yciu opracowanego modelu przeskokow elektronow uzyskano .redni. d.ugo.. przeskoku elektronu r1 = 2.6 nm na podstawie wynikow do.wiadczalnych dla wygrzanej probki nanokompozytu.