High temperature impedance spectroscopy study of non-stoichiometric bismuth zinc niobate pyrochlore

Single phase non-stoichiometric bismuth zinc niobate, Bi3Zn1.84Nb3O13.84 was prepared by a conventional solid state method. The sample was refined and fully indexed on the cubic system, space group Fd3m, Z = 4 with a = 10.5579(4) A. Electrical characterisation was performed using an ac impedance analyser over the temperature range of 25-850 °C and frequency range of 5 Hz - 3 MHz. Typical dielectric response was observed in Bi3Zn1.84Nb3O13.84with high relative permittivity, low dielectric loss and negative temperature coefficient of capacitance, with the values of 147, 0.002 and -396 ppm/°C, at 100 kHz at ambient temperature, respectively. The material is highly resistive, with the conductivity of 10-21 ohm-1ocm-1 and a high activation energy of 1.59 eV.