The analysis of frost resistance of selected modified concretes

In this paper, experimental studies of frost resistance of two types of basalt concrete are presented. The two concrete mixes were unmodified and modified by superplasticizer and silica fume. The influence of two cement matrix modification on the frost resistance of concrete in three kinds of curing condition has been discussed: laboratory conditions, hydroisolated conditions and in water. Analysis of compressive strength and tensile strength at bending after 100 cycles of freezing and thawing was used. Frost resistance was tested at temperatures from +18°C to -20°C. The highest loss of frost resistance was observed in ordinary concrete saturated with water in 100%. The tests showed that apart from modification of concrete microstructure, concrete storage conditions are also important. The testing showed that concrete modified with superplasticizer and microsilica fume is characterized by greater frost resistance compared to normal concrete.

---

W artykule przedstawiono odporność mrozową zwykłego betonu oraz modyfikowanego betonu superplastyfikatorem i mikrokrzemionką. Wpływ modyfikacji na mrozoodporność betonu przedstawiono dla betonów twardniejących w trzech różnych warunkach: laboratoryjnych, hydroizolowanych oraz nasączonych do stałej masy wodą. Analizę wytrzymałości na ściskanie i rozciąganie przy zginaniu przeprowadzono po 100 cyklach zamrażania i rozmrażania. Badanie mrozoodporności przeprowadzono w temperaturze od +18°C do -20°C. Największy spadek odporności mrozowej zaobserwowano dla betonu nasączonego w 100% wodą. W przeprowadzonych badaniach zaobserwowano, iż niezależnie od modyfikacji struktury betonu, równie ważny jest sposób pielęgnacji podczas jego twardnienia. W badaniach wykazano, iż modyfikowany beton charakteryzuje się większą mrozoodpornością w porównaniu z betonem zwykłym.