Thermodynamic properties of the liquid Ag-Bi-Pb solutions

Employing the electrochemical cells with the solid electrolyte (...) at first Gibbs free energy of formation of solid PbO was determined over the temperature range 848-1123K (...). Next, activities of lead in the liquid ternary Ag-Bi-Pb solutions along the cross-section XBi/XPb=1, and for alloy compositions XAg=0.4, 0.5, 0.6, 0.7, 0.8 were measured. Obtained data were used to estimate ternary interaction parameter in the equation describing thermodynamic properties of liquid solutions. Consequently, ternary Ag-Bi-Pb phase diagram was recalculated taking into account the deviation from ldeality of liquid ternary solutions.

---

Stosując odniwa galwaniczne ze stałym elektrolitem (...) wyznaczono najpierw energię swobodną tworzenia stałego tlenku PbO w zakresie temperatur 8481123K (...)Nastepnie wyznaczono aktywność ołowiu w ciekłych stopach potrójnych Ag-Bi-Pb dla składów XAg=0.4, 0.5, 0.6, 0.7, 0.8 przy stałym stosunku składów XPb/XBi=1. Otrzymane wyniki uzyto do wyznaczenia potrójnego parametru oddziaływania w równaniach opisujących właściwości termodynamiczne ciekłej fazy metalicznej. Tak wyznaczone zależności zastosowano w obliczeniach potrójnego układu równowagi biorąc tym samym pod uwagę odstępstwo właściwości roztworów potrójnych od stanu idealnego.