Dynamic viscosity of blast furnace primary and final slag with titanium and alkali admixtures

For the sake of difficulties with changes of the slags absolute viscosity in blast furnace raised of contents of titanium compounds, examinations of this physical quantity were undertaken studies. The main objective of works was the determine of titanium and alkalies compounds on the dynamic viscosity of synthetic blast furnace primary and final slags in the multicomponent systems. Practical studies have been realize on concentric cylinders rotation viscometer methods. Range of temperatures for primary slags: 1200-1300°C, for final slags: 1400-1500°C. The following slags systems were being studies: CaO-SiO2-Al2O3-MgO-FeO-TiO2-(K2O+Na2O) and CaO-SiO2-Al2O3-MgO-TiO2-(K2O+Na2O).

---

Ze względu na trudności związane ze zmianami lepkości dynamicznej żużli w wielkim piecu zawierających podwyższone zawartości związków tytanu, podjęto badania tej wielkości fizycznej. Celem pracy było określenie wpływu związków tytanu i alkaliów na współczynnik lepkości dynamicznej syntetycznych żużli wielkopiecowych w układach wieloskładnikowych dla żużli pierwotnych oraz końcowych. Badania przeprowadzono na wiskozymetrze opartym o metody koncentrycznych cylindrów. Zakres temperatur dla żużli pierwotnych: 1200-1300°C, dla żużli końcowych: 1400-1500°C. Badano następujace układy żużlowe: CaO-SiO2-Al2O3-MgO-FeO-TiO2-(K2O+Na2O) oraz CaO-SiO2-Al2O3-MgO-TiO2-(K2O+Na2O).