Macromolecule crosslink and scission yield under radiation modification of polyethylene

y(ipsylon)-Radiation-induced crosslinking of LDPE over a wide temperature range has been studied. The new loglogarythmic scale method approved very convient to treat data of sol-gel analysis. A straight dependence was always obtained for the plotting of log (sol fraction) against log (dose). Gel poinst were accurately obtained from the plot intersects and scission/crosslinking rations were obtained from the plot slopes using computer simulations which a special software GelSim6. The crosslinking and scission yields were determined to be 0.17 and 0.078 mmol/kJ at 30st.C and they were increased to 2.3 and 4.4 mmol/kJ at 300st.C. The obsreved regularities are explained by considering that the enhanced macromolecular motion decreases the cage effect on recombination reactions in the polymer.

---

Badano sieciowanie LDPE pod wpływem promieniowania y w szerokim zakresie temperatur. Do analizy danych zol-żel bardzo przydatna okazała się nowa metoda oparta na wykorzystaniu skali podwójnie logarytmicznej. Przedstawiając log (ułamek zolu) jako funkcję log (dawka) otrzymuje sie zawsze linię prostą. Punkty żelu wyznacza się z przecięć wykresu, natomiast stosunki pękanie/sieciowanie uzyskuje się z nachylenia wykresu stosując komputerową symulację z użyciem specjalnego programu GelSim6. Wyznaczone wydajności sieciowania i pękania wynoszą odpowiednio 0,17 i 0,078 mmol/kJ w 30 st. C. W temperaturze 300 st. C wzrosły one do 2,3 i 4,4 mmol/kJ. Zaobserwowane prawidłowości można wyjaśnić biorąc pod uwagę fakt, że zwiększona ruchliwość makrocząsteczek zmniejsza wpływ efektu klatkowego na reakcje rekombinacji w polimerze.