Self-Consolidation Mechanism of Ti5Si3 Compact Obtained by Electro-Discharge-Sintering Directly from Physically Blended Ti-37.5 At.% Si Powder Mixture

Characteristics of electro-discharge-sintering of the Ti-37.5at.% Si powder mixture was investigated as a function of the input energy, capacitance, and discharge time without applying any external pressure. A solid bulk of Ti5Si3 was obtained only after in less than 129 μsec by the EDS process. During a discharge, the heat is generated to liquefy and alloy the particles, and which enhances the pinch pressure can condensate them without allowing a formation of pores. Three step processes for the self-consolidation mechanism during EDS are proposed; (a) a physical breakdown of oxide film on elemental as-received powder particles, (b) alloying and densifying the consolidation of powder particles by the pinch pressure, and (c) diffusion of impurities into the consolidated surface.

---