Studies of extrusion of polyethylene with the addition of halloysite nanotubes. Part 1. Characteristics of the extrusion

Low d. polyethylene doped with halloysite nanotubes (diam. 30–70 nm, length 1–3 μm) in concns. 2–6% by mass as well as without additives was extruded in a single-screw lab. extruder at 50 rpm or 150 rpm. The effect of chem. compn. of obtained materials and rotational speed of the screw on the parameters of the extrusion process was tested. The highest efficiency of the process (over 39.6%) was achieved during extrusion at screw speed of 150 rpm of non-doped polymer. The efficiency slightly decreased to 39.1% with the increase of the nanotube content. The smallest value of unit energy consumption was achieved for the extrusion (at 150 rpm) of a material contg. 2% halloysite. The screw rotating at 50 rpm resulted in a significant redn. in the efficiency of the process as well as in significant increase in the unit energy consumption for the tested materials.

EUROPEAN UNION

Polietylen o małej gęstości napełniono haloizytowymi nanorururkami (średnica 30–70 nm, długość 1–3 μm) o udziale masowym 2–6% w stosunku do osnowy oraz bez dodatków, proces wytłaczania przeprowadzono w laboratoryjnej wytłaczarce jednoślimakowej przy prędkościach obrotowych ślimaka 50 rpm i 150 rpm. Zbadano wpływ składnika chemicznego i prędkości obrotowej ślimaka na parametry wytłaczania. Największą wydajność procesu (ponad 39,6%) osiągnięto podczas wytłaczania polimeru nienapełnionego przy prędkości ślimaka 150 rpm. Wydajność nieznacznie spadała (do 39,1%) wraz ze wzrostem zawartości nanorurek. Najmniejszą wartość jednostkowego zużycia energii osiągnięto przy wytłaczaniu (150 rpm) materiału zawierającego 2% haloizytu. Zastosowanie prędkości obrotowej ślimaka 50 rpm spowodowało znaczne zmniejszenie wydajności wytłaczania oraz znaczny wzrost jednostkowego zużycia energii dla badanych materiałów.