Manufacturing Technology and Physical Properties of Yarn Blends Containing Broken Polyester Fibres with Decreased Susceptibility to Pilling

The aim of the investigation presented in this article was to verify the possibility of manufacturing polyester/wool blended yarn (of type PET55/Wo45) which would contain a fraction of polyester fibres with decreased susceptibility to pilling, obtained from a spinning cable prepared by the uncontrolled breaking method. This investigation demonstrated that it is possible to manufacture the above-mentioned yarns on condition that the technological process is modified. The physical properties of single and doubled yarns were tested. An analysis of the results obtained indicated that the majority of quality parameters of the 21 tex 550Z single yarn comply with standard requirements, as well as with the values described bv Uster Statistics at the 50% line. A decrease in the twist number of the 21 tex x 2 doubled yarn from 560 rev./m to the value of520 rev./m, i.e. almost 8%, does not in principle influence the decrease in quality of this yarn.

---

Celem badań było stwierdzenie, czy istnieje możliwość wytwarzania przędz mieszankowych PET55/Wo45 z udziałem włókien poliestrowych otrzymywanych z kabla przędzalniczego przygotowanego metodą rozrywania niekontrolowanego. Badania wykazały, że wytwarzanie wymienionych przędz jest możliwe, pod warunkiem modyfikacji procesu technologicznego. Badano właściwości fizyczne przędz pojedynczych i nitkowanych. Stwierdzono, że większość parametrów jakościowych przędzy pojedynczej 21 tex 550Z spełnia wymagania normy, a także wartości określanych przez USTER Statistics na linii 50%, a obniżenie liczby skrętu w przędzy nitkowanej 21 tex x 2 z wartości 560 obr/min do 520 obr/min. a wiec o prawie 8%. zasadniczo nie powoduje obniżenia jej jakości.