Aliphatic-Aromatic Co-polyesters Received from Poly(ethylene terephthalate) Wastes

The results of research into utilisation of poly(ethylene terephthalate) (PET) wastes are presented in this paper. PET wastes have been subjected to reaction with esters of low-molecular aliphatic dicarboxylic acids to receive co-polyesters (KPEs) with properties dependent on the weight ratio of the particular substrates. For selected weight ratios of the raw-materials used, copolymers characterised by the following parameters have been received: glassy temperature ranging from -24°C up to +40°C, melting temperature from 50°C up to 220°C, crystallisation temperature from 80° C up to 160°C and melt flow index of 3-35 g/10 min. The polymers have had different forms: from elastic and plastic masses, through elastic and hard materials to hard and fragile materials.

---

Przedstawiono wyniki badań nad wykorzystaniem odpadów poli (tereftalanu etylenu) (PET). Odpady PET poddano reakcji z estrami niskocząsteczkowych alifatycznych kwasów dwukarboksylowych, otrzymując kopoliestry (KPEs) o właściwościach zależnych od stosunku wagowego substratów. Dla badanych wagowych stosunków surowców uzyskano kopolimery o temperaturach: zeszklenia w granicach od -24°C do +40°C, topnienia 50-220°C, krystalizacji 80-160°C i wskaźnikach płynięcia 3-35 g/10 min. Polimery miały charakter od elastycznych i plastycznych mas, poprzez elastyczne i twarde, do twardych i kruchych tworzyw.