Investigation of the Process for Obtaining Microfibrids from Natural Polymers

The increase in the application of fibrids in the paper, cosmetic, and medical material industries, as well as in environmental protection, is based on their unique properties, principally their large developed surface. This was the ground to commence our investigation in the Institute of Chemical Fibres into obtaining and processing fibrids [1]. This paper is devoted to microfibrids, i.e. fibrids of a diameter smaller than 10 mm. The influence of the ratio of the spinning solution outflow velocity to the coagulation bath outflow velocity (existing over spinning) on the properties of microfibrids (principally on their dimensions) was tested. Test results of obtaining alginate, alginate-starch, and alginate mixed with keratin microfibrids by the wet method are presented, together with an estimation of their properties. The microscopical analysis carried out proved that the microfibrid diameters are in general below 10 µm.

---

Fibrydy znajdują coraz szersze praktyczne zastosowanie w przemyśle papierniczym, kosmetycznym, medycznym, jak również w ochronie środowiska. Zawdzięczają to swoim unikalnym właściwościom, przede wszystkim bardzo rozwiniętej powierzchni, która w głównej mierze zależy od ich wymiarów. Zbadano wpływ stosunku prędkości wypływu roztworu przędzalniczego do prędkości wypływu kąpieli koagulacyjnej na właściwości mikrofibryd, w tym na ich wymiary. W artykule przedstawiono wyniki badań procesu wytwarzania mikrofibryd alginianawych, alginianowo-skrobiowych i alginianowych z keratyną metodą mokrą spod filiery wraz z oceną ich właściwości. Rejestrowano obraz wytworzonych mikrofibryd. Analiza mikroskopowa wykazała, że średnice mikrofibryd są poniżej 10 µm.