Corrosion behaviour of aluminium alloys and 316L stainless steel in propylene glycol and ethylene glycol water solution

The corrosion behaviour of two aluminium alloys (AA1050 and AA5052) and 316L stainless steel was studied in 30% ethylene glycol and propylene glycol water-based solution. The sample made of 316L stainless steel exhibits the highest corrosion resistance in all testing solutions. It was shown that investigated aluminium alloys show comparable electrochemical behaviour in both water-glycol solutions. In the case of ethylene glycol testing solution higher values of the cathodic and anodic current densities were found for all investigated samples. Therefore, the solution of ethylene glycol is a more corrosive environment compared to the propylene glycol solution.

---

Korozyjne zachowanie się stopów aluminium AA1050 i AA5052, a także austenitycznej stali 316L było badane w 30% roztworach wodnych glikolu etylenowego i glikolu propylenowego. Najwyższą odporność na korozję w tych środowiskach wykazuje stal 316L. Stopy aluminium wykazują podobne elektrochemiczne zachowanie w obu roztworach glikolowych. W roztworze glikolu etylenowego zarówno w obszarze katodowym jak i anodowym obserwuje się wyższe prądy dla badanych stopów. W związku z tym, roztwór glikolu etylenowego jest bardziej agresywnym pod względem korozyjnym niż roztwór glikolu propylenowego.

---

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.