Application of Polyaniline for the Modification of Polylactide Fibres

Polyaniline was deposited on a polylactide nonwoven by the in situ method in the form of emeraldine salt (Green Protonated Emeraldine), i.e. by oxidative polymerisation on the fibre surface. The nonwoven was also padded with a solution of Blue Emeraldine Base. Depending on the type of polyaniline (PANI) deposited, the resulting samples showed different conductance values. Changes in electrical resistance were assessed versus the procedure of final treatment. Thermogravimetric measurements showed an increase in the temperature of decomposition of about 50 °C compared to that of an unmodified sample. The nonwoven with the deposited layer of PANI was overlaid with a layer of complexing polymers by the layer-by-layer method. The effect of such a modification on the electro-conductive (resistance) and sorption properties of nonwovens was examined.

---

Na włókninę z włókien polilaktydowych nanoszono polianilinę metodą in situ w postaci soli emeraldyny (Green Protonated Emeraldine), tj. przez polimeryzację oksydacyjną na powierzchni włókien, oraz napawano włókninę roztworem zasady emeraldyny (Blue Emeraldine Base). Stwierdzono różnice w przewodnictwie próbek w zależności od typu naniesionej polianiliny. Badano zmiany oporności elektrycznej w zależności od sposobu końcowej obróbki. Wykonano pomiary termograwimetryczne i stwierdzono wzrost temperatury rozkładu o koło 50 °C w porónaniu z prókąniemodyfikowaną Na włóninęz naniesionąwarstwąpolianiliny nakłdano warstwy polimeró kompleksująych metodą warstwa-po-warstwie (Layer-by-Layer). Zbadano wpłw takiej modyfikacji na włśiwośi elektroprzewodzące (oporność) i sorpcyjne.