Improving the corrosion resistance of TiAl alloys via modification of their surface using halogens

The paper compares the effectiveness of three different methods of surface modification with halogens with regard to the heat resistance of the Ti-48Al-2Cr alloy. The investigated methods included the deposition of MnCl2 from an aqueous solution, implantation of chlorine ions, and coating with a resin that contained fluorosilane. Oxidation studies were performed in pure air and air containing 1% of SO2. It was observed that the resin with fluorosilane initiates the formation of a protective Al2O3 scale, and that its efficiency increases with temperature. The improvement in the corrosion resistance of the Ti-48Al-2Cr alloy coated with a resin layer was more significant than after either chlorine ion implantation or surface deposition of halides.

---

W pracy porównana została efektywność działania halogenów w zakresie poprawy żaroodporności stopu Ti-48Al-2Cr, przy zastosowaniu trzech różnych metod modyfikacji powierzchniowej: nanoszenia MnCl2 z roztworu wodnego, implantacji jonowej chloru oraz powlekania żywicą zawierającą fluorosilan. Badania utleniania przeprowadzono w powietrzu czystym oraz zawierającym 1% SO2. Stwierdzono, że żywica zawierająca fluorosilan inicjuje powstawanie ochronnej zgorzeliny Al2O3, a efektywność jej działania zwiększa się wraz z temperaturą. Poprawa odporności korozyjnej stopu Ti-48Al-2Cr w wyniku pokrycia go warstwą żywicy była bardziej skuteczna od implantacji jonowej chloru oraz powierzchniowego osadzania halogenków.