Optimization of the Q-P Process Parameters for Low Alloyed Steels with 0.2% C

In steels which are treated by the quenching and partitioning (Q&P) process, carbon content is one of the crucial parameters because carbon contributes greatly to stabilization of retained austenite and strengthens the material. In the present study, the Q&P process was gradually optimised for two low-alloyed steels with 0.2 % carbon content and with and without Cr addition. The results show that the cooling rate, as well as the austenitizing temperature, has a pronounced effect on microstructure evolution. The strength and elongation in the Mn, Si and Cr-alloyed steel was approx. 900 MPa and more than 30 %, respectively.

---

W stalach poddanych obróbce hartowania i partycjonowania (Quenching and Partitioning – Q&P), zawartość węgla jest jednym z kluczowych parametrów, ponieważ węgiel znacząco wpływa na stabilizacje austenitu szczątkowego i umacnia materiał. W niniejszych badaniach obróbka Q&P była stopniowo optymalizowana dla dwóch niskostopniowych stali o zawartości węgla 0, 2% zawierających dodatek chromu oraz bez tego dodatku. Wyniki pokazują wyraźny wpływ szybkości chłodzeniaoraz temperatury austenityzacji na ewolucje mikrostruktury. Wytrzymałość na rozciąganie oraz wydłużenie do zerwania w manganowo-krzemowo-chromowej stali wyniosły odpowiednio ok.900 MPa oraz ponad 30%.