Gas mixtures based on Ar-He for micro-jet cooling after MAG welding
The material selected for this investigation was low alloy weld metal deposit after MAG welding with micro-jet cooling. The present investigation was aimed as the following tasks: obtained WMD with various amount of acicular ferrite in WMD in terms of helium percentage in micro-jet gas mixture. Paper focuses on low alloy steel weld properties after innovate welding method with micro-jet cooling. Weld metal deposit (WMD) for micrograph analyses and impact toughness was carried out for MAG. Until that moment only argon, helium and nitrogen were seriously tested as micro-jet gases. In that paper various gas mixtures (Ar-He) were tested for micro-jet cooling after welding. The influence of oxygen and nitrogen included in gas mixtures based on Ar-He couple on properties of WMD was also tested.
Materiałem wybranym do tego badania było stopiwo uzyskane po spawaniu niestopowej stali procesem MAG z chłodzeniem mikro-jetowym. Badanie miało na celu: otrzymanie stopiwa z różną ilością drobnoziarnistego ferrytu (acicular ferrite) w zależności od zawartości helu w mieszance z argonem stosowanej do schładzania mikro-jetowego. W artykule skoncentrowano się na właściwościach złącza ze stali niestopowej po wprowadzeniu innowacyjnej metody spawania z wykorzystaniem chłodzenia mikro-jetowego. Stopiwo do badań mikrostruktury i udarności było uzyskane po spawaniu procesem MAG. Do tej pory do schładzania mikro-jetowego były dokładnie testowane tylko takie gazy jak argon, hel i azot. W tym artykule badano różne mieszanki gazowe (Ar-He) jako gazy mikro-jetowe. Na własności stopiwa badano również dodatkowy wpływ tlenu i azotu zawartego w mieszankach gazowych opartych na Ar-He.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).