Three point bending of hand laminated fiber composites
The article describes the course and results of research on a composite laminate. Specimens were made from glassreinforced epoxy resin using the hand lamination technique with the fibres arranged unidirectionally along the specimen. The dimensions were selected on the basis of DIN EN ISO 14125. Strain gauges were placed on the surface of every specimen, then testing was conducted - three point bending. The specimen was placed so that the strain gauge was at the stretched side during bending in order to measure the strain. The stress was also calculated analytically, based on the process parameters. As a result, the theoretical stresses were compared with the experimental ones.
Opisano przebieg i wyniki badań laminatu kompozytowego. Materiałem, z którego wykonano próbki, była żywica epoksydowa wzmocniona włóknem szklanym. Próbki do badań zostały przygotowane w technologii laminowania ręcznego. Włókna ułożone były jednokierunkowo, wzdłuż próbki. Wymiary zostały dobrane na podstawie normy DIN EN ISO 14125. Na powierzchni próbki umieszczono tensometry. Następnie przeprowadzono badania - zginanie trójpunktowe. Próbkę umieszczono tak, aby tensometr był od strony rozciągania podczas zginania, dzięki czemu mierzone było odkształcenie. Naprężenia były obliczane również w sposób analityczny, na podstawie parametrów procesu. W wyniku uzyskano porównanie naprężeń teoretycznych z doświadczalnymi.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).